Lube Adhesive & Engineering Co.

GST TAX : 18% INCLUDING 
Thread locking wicking grade,Used for post assembly Application,
Strength : Medium,
Color : Blue
Viscocity : Cps 25 -50
Temperature : -50 to 150

Additional Information:

• Delivery Time: within 2 days
• Packaging Details: 50 ml ,250 ml .5 ltr

Product DescriptionChemical Type Dimethacrylate Ester basedproductViscosity Medium viscous liquidCure AnaerobicApplication Thread lockerStrength HighAnabond 111 is a dimethacrylic ester based highstrength thread locking anaerobic adhesive system,which can cures only in the absence of air andpresence of metal. When applied on to fasteners, itcures to produce fail-safe fastener assemblies.These assemblies can withstand heavy vibrationand resist shock & impact loads. It eliminates theneed for conventional locking methods like star andspring washers, lock plates & nylon nuts. This liquidadhesive is specially designed for locking mild steel,aluminium and passivated bolts & nuts to size up toM20.PROPERTIES OF UNCURED MATERIALColour : RedAppearance : LiquidSpecific Gravity @ 30oC : 1.0 – 1.1Flash point – See MSDSViscosity, Brookfield – DV-I, 30oCSpindle 4 speed 100 rpm, mPas : 1000 - 1500PROPERTIES OF UNCURED MATERIALHandling cure @ RT(M10 Black Bolt & Nut)Minutes 05 – 15Handling cure @ RT(Yellow passivated Bolt to black nut)Minutes 10 – 20Handling cure @ RT(M10 Yellow passivated Bolt toAluminium nut)Minutes < 20Functional cure @ RT(M10 Black Bolt & Nut)Hours 6Breakaway torque @ RT(M10 Black Bolt & Nut)Nm( kgm )31.39 – 39.24( 3.20 – 4.00 )Prevailing torque @RT(M10 Black Bolt & Nut)Nm( kgm )32.37 – 47.08( 3.30 – 4.80 )Breakaway torque @ RT(M10 Yellow passivated Bolt & Nut)Nm(kgm )9.81 ( min.1.0 )Prevailing torque @ RT(M10 Yellow passivated Bolt & Nut)Nm(kgm )11.77 (min.1.20 )Breakaway torque @ RT(M 8 Yellow passivated Bolt & Al.Nut)Nm(kgm )7.85 – 11.77( 0.8 – 1.20 )Prevailing torque @ RT(M8 Yellow passivated Bolt & Al.Nut)Nm(kgm )7.85 – 13.73( 0.8 – 1.40 )Temperature resistance °C -50 to 150

Chemical / Solvent ResistanceOil resistance test is conducted on M10 mild steel nuts& bolts after subjecting to 125°C for different timeintervals. The breakaway torque is evaluated afterspecified time period and percentage strengthretention is given in the following table. Similarexercise is also carried out for petrol and water& glycolat 25°C and 87°CSl.NoEnvironment Temp0C100hrs.500hrs.1000hrs.1.Motor oili) 10 W30ii) 20 W40125100100999999982. Petrol 25 100 95 863.Water / Glycol(50 / 50%)87 96 84 80GENERAL INFORMATIONThis product not recommended for use in pureoxygen or oxygen rich systems and not beselected as a sealant for chlorine or other strongoxidizing materialsFor safe handling information on this product,consult the MSDSApplication:Suitable for locking mild steel, brass, copper,aluminium and passivated metal substrates.FOR ASSEMBLY• Degrease the bolts & nuts (hot/soap waterand solvent) before applying the adhesive.• Cut the tip of the nozzle to the required size.• Squeeze out two to three drops of theadhesive directly on to the threads of thefasteners.• Mate the nuts using a wrench.FOR DISASSEMBLY• Remove with standard hand tools.• Heat the bolt or nut to approximately 2000 Cand disassemble while hot.For cleanup:Cured product can be removed with a combinationof soaking in a solvent and mechanical abrasin suchas a wire brush.Storage Condition:Store the material in its original container in a cooland dry area below 350C. Keep away from heatsource and direct sunlight.Packaging:10 ml, 50 ml, 250 ml & 3.5 ltrs white colour HDPEcontainersShelf life :Fifteen months from the date of manufacture, ifstored at or below 35°C.

Additional Information:

• Production Capacity: available
• Delivery Time: within 2 days
• Packaging Details: 50 ml & 250 ml

GST EXTRA RATE IS 50 ML PACK

LOCTITE® 242®January-2012PRODUCT DESCRIPTIONLOCTITE® 242® provides the following product characteristics:Technology AcrylicChemical Type Dimethacrylate esterAppearance (uncured) Blue liquidLMSFluorescence Positive under UV lightLMSComponents One component -requires no mixingViscosity Medium, thixotropicCure AnaerobicSecondary Cure ActivatorApplication ThreadlockingStrength MediumLOCTITE® 242® is designed for the locking and sealing ofthreaded fasteners which require normal disassembly withstandard hand tools. The product cures when confined in theabsence of air between close fitting metal surfaces andprevents loosening and leakage from shock and vibration.Suitable for applications on less active substrates suchas plated surfaces, where disassembly with hand tools isrequired for servicing. The thixotropic nature of LOCTITE® 242® reduces the migration of liquid product after application to thesubstrate.Mil-S-46163ALOCTITE® 242® is tested to the lot requirements of MilitarySpecification Mil-S-46163A. Note: This is a regional approval.Please contact your local Technical Service Center for moreinformation and clarification.ASTM D5363Each lot of adhesive produced in North America is tested tothe general requirements defined in paragraphs 5.1.1 and5.1.2 and to the Detail Requirements defined in section 5.2.TYPICAL PROPERTIES OF UNCURED MATERIALSpecific Gravity @ 25 °C 1.0Flash Point - See SDSViscosity, Brookfield - RVF, 25 °C, mPa·s (cP):Spindle 3, speed 2 rpm, , Helipath ≥5,000LMSSpindle 3, speed 20 rpm, Helipath 800 to 1,600LMSViscosity, Brookfield - RVT, 25 °C, mPa·s (cP):Spindle 3, speed 20 rpm, *900 to 1,400LMSLubricity, ASTM D5648, K value, ASTM D 5648, %:3/8 x 16 Phosphate & Oil Nuts, Bolts, SteelWasher-10 to 10L
(In critical applications, it is necessary to determine the Kvalues independently. Henkel Corporation makes nowarranty of specific performance on any individualfastener)TYPICAL CURING PERFORMANCECure Speed vs. SubstrateThe rate of cure will depend on the substrate used. The graphbelow shows the breakaway strength developed with time onM10 steel nuts and bolts compared to different materials andtested according to ISO 10964.% of Full Strength on SteelCure Time10075502501min 5min 10min 30min 1h 3h 6h 24hSteelBrassZinc dichromateStainless steelCure Speed vs. TemperatureThe rate of cure will depend on the temperature. The graphbelow shows the breakaway strength developed with time atdifferent temperatures on M10 steel nuts and bolts and testedaccording to ISO 10964.% of Full Strength on SteelCure Time10075502501min 5min 10min 30min 1h 3h 6h 24h
Cure Speed vs. ActivatorWhere cure speed is unacceptably long, or large gaps arepresent, applying activator to the surface will improve curespeed. The graph below shows the breakaway strengthdeveloped with time on M10 zinc dichromate steel nuts andbolts using Activator 7471™ and 7649™ and tested accordingto ISO 10964.
TYPICAL PERFORMANCE OF CURED MATERIALAdhesive PropertiesAfter 1 hour @ 22 °CBreakaway Torque, ISO 10964:3/8 x 16 steel nuts (grade2) and bolts (grade 5)N·m 5.6 to 17LMS(lb.in.) (50 to 150)Prevail Torque, ISO 10964:3/8 x 16 steel nuts (grade2) and bolts (grade 5)N·m 1.7 to 6.8LMS(lb.in.) (15 to 60)

Additional Information:

• Delivery Time: WITHIN 2 DAYS
• Packaging Details: 50 ML & 250 ML

above price is including gst18%
LOCTITE® 222 provides the following product characteristics: Technology Acrylic Chemical Type Dimethacrylate ester Appearance (uncured) Purple liquidLMS Fluorescence Positive under UV lightLMS Components One component - requires no mixing Viscosity Low, thixotropic Cure Anaerobic Secondary Cure Activator Application Threadlocking Strength Low.
LOCTITE® 222 is designed for the locking and sealing of threaded fasteners which require easy disassembly with standard hand tools. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Particularly suitable for applications such as adjustment of set screws, small diameter or long engagement length fasteners, where easy disassembly is required without shearing the screw. The thixotropic nature of LOCTITE® 222 reduces the migration of liquid product after application to the substrate. TYPICAL PROPERTIES OF UNCURED MATERIAL Specific Gravity @ 25 °C 1.05 Flash Point - See SDS Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP): Spindle 3, speed 2.5 rpm, ≥3,500 Spindle 3, speed 20 rpm 900 to 1,500LMS Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP): Shear rate 277 s -1 135 TYPICAL CURING PERFORMANCE Cure Speed vs. Substrate The rate of cure will depend on the substrate used. The graph below shows the breakaway strength developed with time on M10 steel nuts and bolts compared to different materials and tested according to ISO 10964.
Cure Speed vs. Bond Gap The rate of cure will depend on the bondline gap. Gaps in threaded fasteners depends on thread type, quality and size. The following graph shows shear strength developed with time on steel pins and collars at different controlled gaps and tested according to ISO 10123. 

Additional Information:

• Delivery Time: IMMEDIATE
• Packaging Details: 50 ML & 250 ML

PRODUCT DESCRIPTION LOCTITE® Product 270 is a single component anaerobic threadlocking material, which develops  high strength. The product cures when confined in the absence of air between close fitting metal surfaces.TYPICAL APPLICATIONS Prevents loosening through vibration and leakage of threaded fasteners.  Particularly suitable for heavy duty applications such as studs into motor housings, nuts onto studs in pump housings and other fasteners where maximum strength is required.PROPERTIES OF UNCURED MATERIAL    Typical Value Range Chemical Type Dimethacrylate ester Appearance Green, Fluorescent Liquid Specific Gravity @ 25°C 1.1 Viscosity @ 25°C, mPa.s (cP)   Falling Ball D 500 400 to 600   DIN 54453, MV   D = 129 s-1  after t=180secs 500 350 to 700 Flash Point (TCC), °C >93TYPICAL CURING PERFORMANCECure speed vs. substrate The rate of cure will depend on substrate used. The graph below shows the breakaway strength developed with time on M10  steel nuts and bolts compared to different materials and tested according to  ISO 10964.
Cure speed vs. bond gap The rate of cure will depend on the bondline gap. Gaps in threaded fasteners depend on thread type, quality and size. The following graph shows shear strength developed with time on steel  pins and collars at different controlled gaps and tested according to ISO 10123.Cure speed vs.  temperature The rate of cure will depend on the ambient temperature. The following graph shows the breakaway strength developed with time at different temperatures on M10  steel nuts and bolts and tested according to  ISO 10964.Cure speed vs. activator Where cure speed is unacceptably long, or large gaps are present, applying activator to the surface will improve cure speed. The graph below shows breakaway strength developed with time using  ACTIVATOR N and T  on M10 Zinc Dichromate steel nuts  & bolts and tested according to  ISO 10964.TYPICAL PROPERTIES OF CURED MATERIAL Physical Properties Coefficient of thermal expansion, ASTM D696, K-1 80 x10-6 Coefficient of thermal conductivity, ASTM C177, W.m-1K-1 0.1 Specific Heat , kJ.kg-1 K-1 0.3PERFORMANCE OF  CURED MATERIAL (After 24 hr at  22°C on N 10 steel nuts & bolts)Typical Value Range Breakaway Torque, ISO 10964, N.m 26 16 to 36                                                 (in.lb) (230) (140 to 320) Prevail Torque, ISO 10964, N.m 36 22 to 50                                                 (in.lb) (350) (200 to 440) Breakloose Torque, DIN 54454, N.m 40 25 to 55                                                 (in.lb) (330) (220 to 490) Max. Prevail Torque, DIN 54454, N.m 57.5 45 to 70                                                 (in.lb) (510) (400 to 600)TYPICAL ENVIRONMENTAL RESISTANCE Test Procedure : Breakloose Torque, DIN 54454 Substrate: M10 Zinc Phosphate Nuts&Bolts Cure procedure: 1 week at 22°CChemical / Solvent Resistance Aged under conditions indicated and tested at 22°C.Solvent Temp. % Initial Strength retained at 100 hr 500 hr 1000 hr 5000 hrMotor Oil 125°C 85 85 75 75 Leaded Petrol 22°C 100 100 100 100 Brake Fluid 22°C 100 100 100 100 Water/Glycol (50%/50%) 87°C 100 85 85 85 Ethanol 22°C 95 95 95 95 Acetone 22°C 95 95 95 95

Additional Information:

• Delivery Time: AVAILABLE
• Packaging Details: 50 ML & 250 ML

PRODUCTDESCRIPTION LOCTITE® 290™ provides the following product characteristics: Technology Acrylic Chemical Type Dimethacrylateester Appearance(uncured) Green liquidLMS Fluorescence Positive underUVlightLMS Components One component - requiresnomixing Viscosity Low Cure Anaerobic SecondaryCure Activator Application Threadlocking Strength Medium toHighLOCTITE® 290™ is designed for the locking and sealing of threaded fasteners. Because of its low viscosity and capillary action, the product wicks between engaged threads and eliminates the need to disassemble prior to application. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. The product can also fill porosity in welds,castings andpowderedmetalparts.Mil-S-46163A LOCTITE® 290™ is tested to the lot requirements of Military Specification Mil-S-46163A. Note: This is a regional approval. Please contact your local Technical Service Center for more informationandclarification.ASTMD5363 Each lot of adhesive produced in North America is tested to the general requirements defined in paragraphs 5.1.1 and 5.1.2andtothe DetailRequirements definedin section 5.2.NSFInternational Registered to NSF Category P1 for use as a sealant where there is no possibilty of food contact in and around food processing areas. Note: This is a regional approval. Please contact your local Technical Service Center for more informationandclarification.NSFInternational CertifiedtoANSI/NSFStandard61 for use in commercial and residential potable water systems not exceeding 82° C. Note: This is a regional approval. Please contact your local Technical ServiceCenter formore informationandclarification.
TYPICALPROPERTIESOFUNCUREDMATERIAL SpecificGravity @ 25°C 1.08 Flash Point - See SDS Viscosity, Brookfield -RVT, 25°C,mPa·s (cP): Spindle 1, speed50rpm, 20 to55LMS TYPICALCURINGPERFORMANCECureSpeedvs.Substrate The rate of cure will depend on the substrate used. The graph below shows the breakaway strength developed with time on M10 steel nuts and bolts compared to different materials and testedaccordingtoISO10964.
CureSpeedvs.BondGap The rate of cure will depend on the bondline gap. Gaps in threaded fasteners depends on thread type, quality and size. The following graph shows shear strength developed with time on steel pins and collars at different controlled gaps and tested accordingtoISO10123.
CureSpeedvs.Temperature The rate of cure will depend on the temperature. The graph below shows the breakaway strength developed with time at different temperatures on M10 steel nuts and bolts and tested accordingtoISO10964. 
CureSpeedvs.Temperature The rate of cure will depend on the temperature. The graph below shows the breakaway strength developed with time at different temperatures on M10 steel nuts and bolts and tested accordingtoISO10964. 
TYPICALPROPERTIESOFCUREDMATERIAL PhysicalProperties: Coefficient of Thermal Expansion, ISO11359-2, K-180×10-6 Coefficient of Thermal Conductivity, ISO8302, W/(m·K)0.1SpecificHeat, kJ/(kg·K) 0.3TYPICALPERFORMANCEOFCUREDMATERIAL AdhesivePropertiesAfter 24 hours @ 22°C Breakaway Torque, ISO 10964: M10 steel nuts and bolts      N·m         10      (lb.in.)     (90)Prevail Torque, ISO 10964: M10 steel nuts and bolts      N·m         29      (lb.in.)     (260) Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m: M10 steel nuts and bolts      N·m         30      (lb.in.)

Additional Information:

• Delivery Time: WITHIN TWO DAYS

ABOVE PRICE IS INCLUDING GST 18%.
PRODUCT : FEVICOL ANR 138DESCRIPTION: Fevicol ANR 138 is a high strength anaerobic formulation ideally designed tolock reliably larger diameter studs for secured locking of studs. The product is designedspecially with higher gap filling capacity.PRODUCT FEATURES:· Single component· High Strength· Solventless· Fills gaps up to 0.25 mm· Long shelf life· Good resistance to all usual fluids, gases, chemicals· Temperature resistance up to 180oC· Prevents thread corrosion.APPLICATION AREAS: Fevicol ANR 138 is recommended for securely locking of studs such as anchor studs andlarger diameter studs. It is suitable for high strength thread locking applications.TYPICAL PROPERTIES:Sr. No. Properties Unit Typical Data1 Appearance Visual Green Clear Liquid.2 Viscosity @ 30 Deg.C Poise 23 – 273 Minutes 5-204 250-4505 150-300
METHOD OF APPLICATION:1. Surface Preparation: Clean the metal surface with clean cotton cloth to remove dustand with solvent to remove oil, grease etc. Degreasing solvent like Trichloroethylene canbe used to remove oil and grease effectively.2. Apply Fevicol ANR 138 to the metal surfaces uniformly in sufficient quantity by squeezing.3. Ensure that quantity of the material is sufficient.4. Assemble uniformly so that no air bubbles are trapped. Full strength obtained after 24hours of curing time at ambient conditions.CURING:Speed of curing depends on various factors such as:Type of Metal :Copper & brass – Very fastSteel -- FastPure Aluminium – SlowCuring is slow on some plated surfaces like Zinc and cadmium.Temperature : Higher the temperature (upto 55 oC) faster the cure & vice versa.Gap Filling : Thin bond line cures faster than thick bond line.DISASSEMBLY OF ADHESIVE BOND:Parts assembled using Fevicol ANR 136 can be disassembled simply by using ordinary tools.CLEANING OF TOOLS: Tools can be cleaned by Solvents like Acetone immediately after use.HANDLING:· Fevicol ANR 138 is non-toxic.· A soap water wash after handling is sufficient.· For details please refer to our MSDS.STORAGE: Fevicol ANR 138 is to be stored away from heat, sunlight & moisture in a cooldark place.SHELF LIFE: The Shelf life in the original sealed packing is 15 months from manufacturewhen stored as per instructions mentioned above.PACKING: 50 ml, 250ml, Plastic bottles.

Additional Information:

• Delivery Time: IMMEDIATE
• Packaging Details: 250 ML

ABOVE PRICE IS INCLUDING GST18%
PRODUCT DESCRIPTION Fasto LockSeal HS is high strength, anaerobic thread locker & sealant. LockSeal HS cures when confined in the absence of air on close-fitting metal surfaces. LockSeal HS is slightly oil tolerant, so it will bond some ‘as received’ parts, but best results are obtained with clean substrates. LockSeal HS to be used for locking & sealing where high strength opening is required. LockSeal HS prevents corrosion of assembled parts.TYPICAL APPLICATIONSFasto LockSeal HS is suitable for most medium and coarse threads. Fasto LockSeal HS is formulated to lock & seal all metric and imperial nuts and bolts, preventing vibration loosening and leakage through the threads. LockSeal HS is typically used in crushers, diesel generators, agricultural machines, Hydraulic assemblies, heavy engineering machineries and many more industrial & automobile assemblies.TYPICAL APPLICATIONSFasto LockSeal HS is suitable for most medium and coarse threads. Fasto LockSeal HS is formulated to lock & seal all metric and imperial nuts and bolts, preventing vibration loosening and leakage through the threads. LockSeal HS is typically used in crushers, diesel generators, agricultural machines, Hydraulic assemblies, heavy engineering machineries and many more industrial & automobile assemblies.TYPICAL CURING PERFORMANCECure speed vs. Temperature All figure relating to cure speed are tested at 21°C. Lower temperatures will result in slower cure. Heating the assembled part accelerates the curing process. Activator Fasto AP49 should be used when the temperature is less than 5°C. Cure speed vs. bond gap The size of the bond gap greatly affects the speed of cure of anaerobic adhesives. Bond gap varies with thread type and size of the fastener. The larger the gap between surfaces, the slower the cure speed. Maximum recommended gap for Fasto LockSeal HS is 0.15mm. Cure speed vs. Substrate Cure speed and strength vary according to the substrates. When used on mild steel and brass components Fasto LockSeal HS will reach full strength more rapidly than on more inert materials such as stainless steel and zinc dichromate. Anaerobic Adhesives only cure in the absence of air with metal part activation. Cure speed vs. Activator Where speed is too slow or the bond gap is very large, Fasto AP49 Activator may be used to accelerate cure speed. The use of an accelerator may reduce bond strength up to 30%. Fasto recommends testing on the parts of measure the effect. TYPICAL ENVIRONMENTAL RESISTANCE Hot strength Fasto LockSeal HS is suitable for use at temperatures up to 150°C. At 150°C the bond strength will be ~45% of the strength of at 21°C.Heat ageingFasto LockSeal HS retains over 90% full strength when heated to 100°C for 90 days then cooled and tested at 21°C. Chemical / Solvent Resistance Fasto LockSeal HS exhibit excellent chemical resistance to most oils and solvents including motor oil, leaded petrol, brake fluid, acetone, ethanol, propanol and water. Anaerobic adhesives and sealants are not recommended for use in pure oxygen and chlorine lines 

Additional Information:

• Delivery Time: READY STOCK
• Packaging Details: 50 ML & 250 ML

GST 18% INCLUDING

Thread locking, Stud grade under M 20 size

Strength : HighThread locking, Stud grade under M 20 size

Strength : High

Colour : Red

Viscosity (cPs) : 275 -325

Temperature resistance : -50 to +150 ° C

Typical Application : Locking of Studs and Bolts under M20 size

Colour : Red

Viscosity (cPs) : 275 -325

Temperature resistance : -50 to +150 ° C

Typical Application : Locking of Studs and Bolts under M20 size

Additional Information:

• Delivery Time: within 2 days
• Packaging Details: 50 ml ,250 ml ,3.5 ltr pack

ABOVE PRICE IS INCLUDING GST 18%
LOCTITE® 243™ provides the following product characteristics: Technology Acrylic Chemical Type Dimethacrylate ester Appearance (uncured) Blue liquidLMS Fluorescence Positive under UV lightLMS Components One component - requires no mixing Viscosity Medium, thixotropic Cure Anaerobic Secondary Cure Activator Application Threadlocking Strength Medium This Technical Data Sheet is valid for LOCTITE® 243™ manufactured from the dates outlined in the "Manufacturing Date Reference" section LOCTITE® 243™ is designed for the locking and sealing of threaded fasteners which require normal disassembly with standard hand toolsThe product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibrationThe thixotropic nature of LOCTITE® 243™ reduces the migration of liquid product after application to the substrateLOCTITE® 243™ provides robust curing performance. It not only works on active metals (e.g. brass, copper) but also on passive substrates such as stainless steel and plated surfacesThe product offers high temperature performance and oil tolerance. It tolerates minor surface contaminations from various oils, such as cutting, lubrication, anti-corrosion and protection fluids NSF International Registered to NSF Category P1 for use as a sealant where there is no possibilty of food contact in and around food processing areas. Note: This is a regional approval. Please contact your local Technical Service Center for more information and clarification. NSF International Certified to ANSI/NSF Standard 61 for use in commercial and residential potable water systems not exceeding 82° C. Note: This is a regional approval. Please contact your local Technical Service Center for more information and clarification.
TYPICAL PROPERTIES OF UNCURED MATERIAL Specific Gravity @ 25 °C 1.08 Flash Point - See SDS Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP): Spindle 3, speed 20 rpm 1,300 to 3,000LMS Viscosity, Cone & Plate, 25 °C, mPa·s (cP): Cone 35/2°Ti @ shear rate 129 s -1 350Prevail Torque @ 180°, ISO 10964, Unseated:M10 black oxide bolts and mild steel nuts N·m 5 (lb.in.) (40) M6 black oxide bolts and steel nuts N·m 1 (lb.in.) (8) M16 black oxide steel bolts and mild steel nuts N·m 13 (lb.in.) (115) 3/8 x 16 steel nuts and bolts N·m 3 (lb.in.) (26) Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m: M10 black oxide bolts and mild steel nuts N·m 24 (lb.in.) (210) 3/8 x 16 steel nuts and bolts N·m 15 (lb.in.) (130) Prevail Torque @ 180°, ISO 10964, Pre-torqued to 5 N·m: M10 black oxide bolts and mild steel nuts N·m 4 (lb.in.) (35) 3/8 x 16 steel nuts and bolts N·m 3.5 (lb.in.) (30) Compressive Shear Strength, ISO 10123: Steel pins and collars N/mm² ≥7.6LMS (psi) (≥1,100) Cured for 1 week @ 22 °C Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m: M10 zinc phosphate nuts and bolts N·m 26 (lb.in.) (230) M10 stainless steel nuts and bolts N·m 17 (lb.in.) (150)

Additional Information:

• Delivery Time: IMMEIDATE BASIS
• Packaging Details: 50ML & 250 ML

1.1. Product identifier LOCTITE® 277™ THREADLOCKER HIGH STRENGTH Contains: Cumene hydroperoxide 1.2. Relevant identified uses of the substance or mixture and uses advised against Intended use: Anaerobic Adhesive 1.3. Details of the supplier of the safety data sheet Henkel Ltd Wood Lane End HP2 4RQ Hemel Hempstead Great Britain Phone: +44 1442 278000 Fax-no.: +44 1442 278071 ua-productsafety.uk@uk.henkel.com 1.4. Emergency telephone number 24 Hours Emergency Tel: +44 (0)1442 278497 SECTION 2: Hazards identification 2.1. Classification of the substance or mixture Classification (CLP): Serious eye irritation Category 2 H319 Causes serious eye irritation. Specific target organ toxicity - single exposure Category 3 H335 May cause respiratory irritation. Target organ: respiratory tract irritation 2.2. Label elements Label elements (CLP): Hazard pictogram: Signal word: Warning MSDS-No.: 153485 V003.2 LOCTITE® 277™ THREADLOCKER HIGH STRENGTH Page 2 of 10 Hazard statement: H319 Causes serious eye irritation. H335 May cause respiratory irritation. Precautionary statement: ***For consumer use only: P101 If medical advice is needed, have product container or label at hand. P102 Keep out of reach of children. P501 Dispose of waste and residues in accordance with local authority requirements*** Precautionary statement: Prevention P261 Avoid breathing vapours. Precautionary statement: Response P337+P313 If eye irritation persists: Get medical advice/attention. 2.3. Other hazards None if used properly. Not fulfilling Persistent, Bioaccumulative and Toxic (PBT), very Persistent and very Bioaccumulative (vPvB) criteria. SECTION 3: Composition/information on ingredients 3.2. Mixtures General chemical description: Methacrylate resin based threadlocker Declaration of the ingredients according to CLP (EC) No 1272/2008: Hazardous components CAS-No. EC Number REACH-Reg No. content Classification Cumene hydroperoxide 80-15-9 201-254-7 >= 1- < 2,5 % Acute Tox. 4; Dermal H312 STOT RE 2 H373 Acute Tox. 4; Oral H302 Org. Perox. E H242 Acute Tox. 3; Inhalation H331 Aquatic Chronic 2 H411 Skin Corr. 1B H314 N,N-Diethyl-p-toluidine 613-48-9 210-345-0 > 0,1- < 0,9 % Acute Tox. 3; Oral H301 Acute Tox. 3; Dermal H311 Acute Tox. 3; Inhalation H331 STOT RE 2 H373 Aquatic Chronic 3 H412 N,N-dimethyl-o-toluidine 609-72-3 210-199-8 > 0,1- < 0,5 % Acute Tox. 3; Inhalation H331 Acute Tox. 3; Dermal H311 Acute Tox. 3; Oral H301 STOT RE 2 H373 Aquatic Chronic 3 H412 For full text of the H - statements and other abbreviations see section 16 "Other information". MSDS-No.: 153485 V003.2 LOCTITE® 277™ THREADLOCKER HIGH STRENGTH Page 3 of 10 Substances without classification may have community workplace exposure limits available. SECTION 4: First aid measures 4.1. Description of first aid measures Inhalation: Move to fresh air. If symptoms persist, seek medical advice. Skin contact: Rinse with running water and soap. Seek medical advice. Eye contact: Rinse immediately with plenty of running water (for 10 minutes). Seek medical attention if necessary. Ingestion: Rinse out mouth, drink 1-2 glasses of water, do not induce vomiting. Seek medical advice. 4.2. Most important symptoms and effects, both acute and delayed EYE: Irritation, conjunctivitis. RESPIRATORY: Irritation, coughing, shortness of breath, chest tightness. 4.3. Indication of any immediate medical attention and special treatment needed See section: Description of first aid measures SECTION 5: Firefighting measures 5.1. Extinguishing media Suitable extinguishing media: Carbon dioxide, foam, powder Fine water spray Extinguishing media which must not be used for safety reasons: None known 5.2. Special hazards arising from the substance or mixture In the event of a fire, carbon monoxide (CO) and carbon dioxide (CO2) can be released. In case of fire, keep containers cool with water spray.

Additional Information:

• Delivery Time: within 2 days
• Packaging Details: 50 ml & 250 ml

ABOVE PRICE IS INCLUDING GST 18%

 DESCRIPTION:  Fevicol ANR 124  is a high strength anaerobic formulation ideally designed for secured locking of studs.  Fevicol ANR 124 enables faster installation of studs.

PRODUCT FEATURES:

· Single component

· High Strength

· Solventless

· Fills gaps upto 0.25 mm

· Long shelf life

· Good resistance to all usual fluids, gases, chemicals

· Temperature resistance upto 150^oC

· Prevents thread corrosion.

APPLICATION AREAS:

· Fevicol ANR 124 is recommended for securely locking of studs such as anchor studs and larger diameter studs.  It is suitable for high strength thread locking applications.

 TYPICAL PROPERTIES:

 1) Appearance : Red Clear Liquid.

2) Viscosity at 30 ^oC : 8 – 10 poise.

3) Setting Time at ambient on

i)  MS M10 Nuts & Bolts :  5 -  20 minutes

4) Breakaway Torque at ambient

on

i)  MS M10 Nuts & Bolts :  150 - 300 kg.cm

5) Prevailing Torque at ambient on

i)  MS M10 Nuts & Bolts : 100 - 250 kg.cm

 Above typical values should not be construed as specifications.

..2/-          Pg.no. 2 of 2

 METHOD OF APPLICATION:

1. Surface Preparation:  Clean the metal surface with clean cotton cloth to remove dust and with solvent to remove oil, grease etc.  Degreasing solvent like Trichloroethylene can be used to remove oil and grease effectively.

2. Apply Fevicol ANR 124 to the metal surfaces uniformly in sufficient quantities by squeezing.

3. Assemble uniformly so that no air bubbles are trapped.  Ensure that quantity of the material is sufficient.

 CURING:

Speed of curing depends on various factors such as:

 

Type of Metal  :  Copper & brass – Very fast

                           Steel                   - Fast

                           Pure Aluminium – Slow

 

Additional Information:

• Delivery Time: within 2 days
• Packaging Details: 50 ML & 250 ML

ABOVE PRICE IS INCLUDING GST 18%.

DESCRIPTION: Fevicol ANR 146 is a low viscosity anaerobic thread locker speciallydesigned for sealing & locking of fasteners & adjusting screws in place after assembly.Due to lower viscosity and good capillary action it penetrates in to micro porosities & hairline cracks in castings, sintered metal parts etc.PRODUCT FEATURES:· Single component· Solventless· Fills gaps upto 0.1 mm· Long shelf life.· Good resistance to all usual fluids, gases, chemicals· Temperature resistance upto 150 o CAPPLICATION AREAS:As a medium strength locking & sealing compound for assembled nuts, bolts & studs,Sealing of welded fine porous lines. It has good capillary action & good penetration power.It also strengthens press fit joints.TYPICAL PROPERTIES: (Tested as per IS 13055:1991)Sr.No Properties Unit Typical Data1 Appearance GreenClear Liquid.2Viscosity at 30 o C( Brookfield Viscometer –RVT,Spidle#1, 20rpm)Centipoise 15253 Specific Gravity @ 30 o C 1.1+/0.054 Setting Time on M10 MSNuts & Bolts at R.T. minutes 3205 Breakloose Torque onMS M10 Nuts & Bolts at R.T. Kgf.cm 80 2006 Prevailing Torque onM10 Nuts & Bolts at R.T. Kgf.cm 100 2507 Static shear strength on MS pin &collar after 24 hrs at ambient temp.Kg/cm 280 minimum.CURING SPEED:There are many factors that affect the speed of cure of anaerobic adhesive, viz. Type ofMetal substrate, Size of gap, The degree of cleanliness of the bonding surface and theweather temperature.¨ METAL TYPE: Copper and Brass surfaces provide rapid cure whereas Mild Steel,Industrial Aluminium are fast to medium speed while Pure Aluminium, Zinc, cadmiumand some passivated metals show slow cure speeds. Care should be taken whendealing with Copper & brass components to avoid cure midway during assembly.¨ GAP: Thinner gaps provide faster cure visàviswider gaps.¨ CLEANLINESS: Curing is faster on clean surfaces. Contaminants such as Oil,Grease etc. slow down the curing.¨ TEMPERATURE: Higher the weather temperature faster the cure speed.TEMPERATURE RESISTANCE: The cured adhesive forms a thermoset bond. Thecured mass will not melt with heat. It’s operating temperature range is –60 to 150 0 C.CHEMICAL/ SOLVENT RESISTANCE: The cured adhesive has good resistance to oils,diesel, petrol, refrigerants, LPG, some solvents etc.CORROSION PREVENTION: The cured adhesive film in the joints will inhibit theelectrolytic corrosion (even bimetallic corrosion) process due to its electrical insulatingproperties. Not only this saves loss of component due to corrosion, but also avoidsseizing, the problem of dismantling at a later time.DISASSEMBLY OF BONDED PARTS: Metallic parts assembled with Fevicol ANR146can be separated without damaging the component by using standard hand tools.METHOD OF APPLICATION:1. Clean the metal parts to get rid of Oil, Grease and other Contaminants. SolventTrichloroethylene or Acetone as Degreasing Agent, is recommended for betterresults.2. Apply adequate quantity of adhesive on all the engaged threads of the bolt andfasten the nut ensuring proper distribution of adhesive in the bond area. Tighten thenut with an appropriate tool.3. Excess material is wiped off. Excess material exposed to air will not solidify.SAFTY & HANDLING:· Fevicol ANR 146 is nontoxic.· A soap water wash after handling is sufficient.· For details please refer to our MSDS.STORAGE: Store below 30 0 C, in a cool & dark place , away from heat, sunlight & moisture.SHELFLIFE:At least 15 months from the date of manufacture in original sealed condition if storedunder recommended storage conditions.

Additional Information:

• Delivery Time: within 2 days
• Packaging Details: 50 ML & 250 ML

ABOVE PRICE IS INCLUDING GST 18%
PRODUCT DESCRIPTION LOCTITE® 271™ provides the following product characteristics: Technology Acrylic Chemical Type Dimethacrylate ester Appearance (uncured) red LMS Fluorescence Positive under UV lightLMS Components One component - requires no mixing Viscosity Low Cure Anaerobic Secondary Cure Activator Application Threadlocking Strength High LOCTITE® 271™ is designed for the permanent locking and sealing of threaded fasteners. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include the locking and sealing of large bolts and studs (up to M25 )
Mil-S-46163A LOCTITE® 271™ is tested to the lot requirements of Military Specification Mil-S-46163A. Note: This is a regional approval. Please contact your local Technical Service Center for more information and clarification. ASTM D5363 Each lot of adhesive produced in North America is tested to the general requirements defined in paragraphs 5.1.1 and 5.1.2 and to the Detail Requirements defined in section 5.2.UL Classification Classified by Underwriters Laboratories Inc.® MH8007 - Fire hazard is small. No flash point in liquid state. Ignition temperature 304°C. For use in devices handling gasoline, petroleum oils, natural gas (pressure not over 300 PSIG), butane and propane not exceeding 2 in. pipe size. Note: This is a regional approval. Please contact your local Technical Service Center for more information and clarificationTYPICAL PROPERTIES OF UNCURED MATERIAL Specific Gravity @ 25 °C 1.1 Flash Point - See MSDS Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP): Spindle 1, speed 10 rpm 400 to 600LMSCure Speed vs. Activator Where cure speed is unacceptably long, or large gaps are present, applying activator to the surface will improve cure speed. The graph below shows the breakaway strength developed with time on M10 zinc dichromate steel nuts and bolts using Activator 7471™ and 7649™ and tested according to ISO 10964.TYPICAL PERFORMANCE OF CURED MATERIAL Adhesive Properties After 90 minutes @ 22 °C Breakaway Torque, ISO 10964: 3/8 x 16 steel nuts (grade 2) and bolts (grade 5) N·m 8.5 to 25.4LMS (lb.in.) (75 to 225) Prevail Torque, ISO 10964: 3/8 x 16 steel nuts (grade 2) and bolts (grade 5) N·m 16.9 to 34LMS (lb.in.) (150 to 300) After 24 hours @ 22 °C Breakaway Torque, ISO 10964: 3/8 x 16 steel nuts (grade 2) and bolts (grade 5) N·m 16.9 to 34LMS (lb.in.) (150 to 300) 3/8 x 16 cadmium nuts and bolts N·m 4.5 to 14.1LMS (lb.in.) (40 to 125) 3/8 x 16 zinc nuts and bolts N·m 4.5 to 14.1LMS (lb.in.) (40 to 125) M10 steel nuts and bolts N·m 17 to 40 (lb.in.) (150 to 350) Prevail Torque, ISO 10964: 3/8 x 16 steel nuts (grade 2) and bolts (grade 5) N·m 22.6 to 40LMS (lb.in.) (200 to 355) 3/8 x 16 cadmium nuts and bolts N·m 16.9 to 34LMS (lb.in.) (150 to 300) 3/8 x 16 zinc nuts and bolts N·m 16.9 to 34LMS (lb.in.) (150 to 300) M10 steel nuts and bolts N·m 23 to 40 (lb.in.) (200 to 350)

Additional Information:

• Delivery Time: READY STOCK
• Packaging Details: 50 ML & 250 ML

ABOVE PRICE IS INCLUDING GST 18%
We are a renowned organisation in the industry to provide our patrons with the best quality range of ANR 138 Thread Lockers.

Details:

• These are high, medium and low strength anaerobic formulations specially designed to seal and lock studs, nuts, bolts and small screws. Wicking grades are specially developed for preassembled parts.
• These products wick between engaged threads and eliminated the need to disassemble prior to application.

Additional Information:

• Delivery Time: within 2 days

ABOVE PRICE INCLUDING GST 18%
Features:

• Withstand heavy vibrations
• Prevent corrosion
• Can be used for high strength applications
• Can be dismantled with mechanical tools
• Superior to conventional locking devices
• Replace traditional locking methods
• Lower cost
• Higher reliability

Additional Information:

• Delivery Time: within 2 days

ABOVE PRICE IS INCLUDING GST 18%
With an objective to fulfill the ever-evolving demands of our clients, we are engaged in offering a wide assortment of ANR 136 Thread Lockers.

Details:

• These are high, medium and low strength anaerobic formulations specially designed to seal and lock studs, nuts, bolts
• and small screws.
• Wicking grades are specially developed for preassembled parts.
• These products wick between engaged threads and eliminated the need to disassemble prior to application.

Features :

• Withstand heavy vibrations
• Prevent corrosion
• Can be used for high strength applications
• Can be dismantled with mechanical tools
• Superior to conventional locking devices
• Replace traditional locking methods
• Lower cost
• Higher reliability

Additional Information:

• Delivery Time: within 2 days

With an impressive growth record in this highly competitive industry, we are providing a qualitative range of Fasto A143 Thread Locking Adhesive.

Additional Information:

• Item Code: Fasto-A143

Being a prominent firm in this domain, we are engaged in offering a distinguished assortment of Fasto A122 Thread Locking Adhesive.

Additional Information:

• Item Code: Fasto-A122

For catering the variegated demands of our respected clients, we are highly engrossed in providing a wide range of Fasto A170 Thread Locking Adhesive.

Details:

• Fasto A170 is fast curing thread locking compound that where regular removal for maintenance is not required.
• It is recommended for permanently locking of studs on engine blocks and pump housings.

Price:

 

Additional Information:

• Item Code: Fasto-A170

Features:

• Very low viscosity
• Wicking capability
• Provide 100% leak free seal
• Purity
• Accurate composition

Price:

Additional Information:

• Item Code: Fasto-A190

Features:

• High viscosity
• High temperature
• Large fastener
• Accurate composition
• Eco friendliness

Price:

Additional Information:

• Item Code: Fasto-A172

Features:

• High strength
• Large bolts & studs
• Precise chemical composition
• High temperature resistance
• Easy to apply

Price:

 

Additional Information:

• Item Code: Fasto-A177

We are highly acclaimed in this industry for providing an optimum quality range of Fasto A162 Thread Locking Adhesive.

Additional Information:

• Item Code: Fasto-A162

ABOVE PRICE IS INCLUDING GST 18%.
Description 3M™ Stainless Steel Cleaner and Polish is a ready-to-use cleaner and polish packaged in an aerosol container. The product is dispensed as a white, non-evaporating foam.Special Features  Cleans and polishes in one step  Leaves no greasy build-up on surfaces  Pleasant citrus fragrance  Leaves a light protective film  Masks blemishes  Slows resoiling  Reduces fingerprinting  Resists streaking  Empty containers may be disposed of in sanitary landfills in accordance with local regulations  NSF® Certified for use in federallyinspected meat and poultry processing plants Applications  Suitable for use on stainless steel, chrome, architectural aluminum, and other interior metal surfaces  Not intended as a glass cleaner.
Packaging  21-ounce (600 g) aerosol can  10-ounce aerosol can  12 cans per case General Use Directions Light soil 1. Shake can well. 2. Turn spray tip so arrow points to dot on can rim. 3. Hold can upright 6-12 inches from surface. 4. Spray area lightly directly on surface or on a clean, dry cloth. 5. Wipe area and polish until dry. Heavy soil 1. Spray 3M™ Stainless Steel Cleaner and Polish onto a Scotch-Brite™ Light Duty Scrubbing Pad 9030 or Scotch-Brite™ Light Duty Scrub Sponge 63. 2. Vigorously rub the surface to remove the heavy soil. Always rub stainless steel in the direction of the grain. 3. Wipe surface with a clean, dry cloth to remove any excess cleaner. 4. Using a clean dry cloth, buff in the direction of the grain to achieve maximum shine. 

Additional Information:

• Delivery Time: READY STOCK
• Packaging Details: 600 ML