Model Grade | MOLYKOTE D321 R ANTIFICTION COATING |
Usage/Application | Metal combinations withfast to medium movement and high load |
Form | Spray |
Unit Pack Size | 400 ML |
Packaging Type | BOTTLE |
Used for improvement the running in process and for lubrication | 400 ml |
ABOVE PRICE IS INCLUDING GST 18%
Air-curing dry-film lubricant Features & benefits • Air drying • Avoidance of stick-slip • High aging resistance Composition • Solid lubricants • Solvents • Binder
Applications For metal/metal combinations with slow to medium fast movements and high loads. Suitable for the permanent lubrication of highly stressed sliding guides with low sliding speeds, oscillating movements or intermittent operation. Used for improving the running-in process and for lubrication under high vacuum and at extreme temperatures. Used successfully for cylinder-head bolts, toaster guides, car mirror adjustment mechanisms, high voltage switches, for the running-in of highly stressed gear wheel. Emergency lubricant for parts of the rotor head of wind energy installations and for groove-free cold extrusion of steel. How to use Surface preparation First, clean and degrease the surface that will be coated with MOLYKOTE® D-321 R Anti-Friction Coating. Phosphatization or sandblasting (180 grit) increases the adhesion and service life.
How to apply Stir MOLYKOTE® D-321 R Anti-Friction Coating thoroughly before applying by spraying or brushing. Recommended dry-film thickness: 5 to 20 µm. Drying Time After 5 minutes at 23°C, the applied film of MOLYKOTE® D-321 R Anti-Friction Coating is touch-dry; this process time can be reduced to 1 minute by exposing the coated part to hot air at 80°C.
Typical properties Specification writers: These values are not intended for use in preparing specifications. Please contact your local MOLYKOTE® sales representative prior to writing specifications on this product. Standard(1) Test Unit Result Color Gray-black Physical properties ISO 2431 Viscosity at 23°C (#3 cup) seconds 23 DIN 53217/2 Density at 20°C g/ml 1.07 CTM 0242 I Nonvolatile content % 29 Temperature Service temperature range °C -180 to 450 Load-carrying capacity, wear protection, service life ASTM D2625 Falex load-carrying capacity(2) N b = 4,500 p = 12,500 s = 6,800 ASTM D2714 LFW-l, rotating(2) F = 2,860 N, n = 72 minutes(2), V = 7.9 m/minute No. of revolutions x 1,000 to µ = 0.1 b = 212 p = 146 s = 306 (1)ISO: International Standardization Organization DIN: Deutsche Industrie Norm. CTM: Corporate Test Method, copies of CTMs are available on request. ASTM: American Society for Testing and Materials (2) Surface pretreatment: b = blank, p = phosphated, s = sand blasted.